Product description of magnesia chrome bricks
Magnesia chrome bricks are alkaline refractories, which generally use magnesia (MgO content 89%~92%) and chromate as raw materials. Magnesia chrome bricks refer to magnesia chrome bricks with light burning magnesia and imported blackstone.
Features of magnesia chrome bricks
Magnesia chrome brick has high fire resistance, strong alkali resistance, good thermal stability and acid resistance slag.
Application of magnesia chrome bricks
Magnesia chrome bricks are mainly used in metallurgical industries such as electric furnace roof, external refining furnace and various nonferrous metal smelting furnaces. Molten magnesia chrome bricks are used for the high temperature part of the furnace wall of the ultra-high power electric furnace. The magnesia chrome bricks made of synthetic materials are used for the high erosion area of the external refining furnace. The magnesia chrome bricks made of synthetic materials are used for the high erosion area of the nonferrous metal flash furnace. In addition, it is also used for the sintering zone of cement rotary kiln and the regenerative chamber of glass kiln.
Parameters of magnesia chrome bricks
| Model | MGe6 | MGe8 | MGe12 | MGe16 | DMGe4 | DMGe8 | DMGe12 | DMGe16 |
| MgO % | 80 | 72 | 70 | 65 | 85 | 77 | 74 | 69 |
| Cr2O3 % | 7 | 10 | 13 | 17 | 5.5 | 9.1 | 14 | 18 |
| CaO % | 1.2 | 1.2 | 1.2 | 1.2 | 1.1 | 1.4 | 1.2 | 1.2 |
| SiO2 % | 3.4 | 4 | 4 | 4.2 | 1.3 | 1.2 | 1.2 | 1.5 |
| Al2O3 % | 4.5 | 6.5 | 6 | 6 | 3.5 | 4 | 3.5 | 4.5 |
| Fe2O3 % | 4 | 4.8 | 5.5 | 6.5 | 3 | 6.4 | 5 | 5.7 |
| Apparent Porosity % | 17 | 18 | 18 | 18 | 18 | 18 | 18 | 18 |
| Bulk Density g/cm3 | 3 | 3 | 3.02 | 3.05 | 3.02 | 3.04 | 3.06 | 3.08 |
| Cold Crushing Strength Mpa | 55 | 55 | 55 | 50 | 50 | 50 | 55 | 55 |
| Refractoriness Under Load °C | 1600 | 1600 | 1600 | 1600 | 1700 | 1700 | 1700 | 1700 |
| Thermal expansion % 1000°C | / | / | / | / | 1 | 1 | 1 | 0.9 |
| Thermal expansion % 1600°C | / | / | / | / | 1.8 | 1.8 | 1.8 | 1.6 |